top of page

Concept 360® - open system cobalt chrome milling and sintering

Concept 360® is a pre-sintered, non-distortinggreen machining open system solution for metal dental frameworks including both single units and bridges.

 

Disc sizes: 98mm x 12mm / 14mm / 16mm

Why use Concept 360® milling discs and the Inertherm® argon sintering furnace?

 

  • NO BINDER! Much more robust than similar products on the market. 

  • in the pre-sintered state it is almost but not quite metallic

  • very easy to machine large frameworks with no distortion

  • open system for an economical solution

  • medical implant Class 2a grade CoCr alloy (composition ISO 5832-4) for ultimate biocompatibility

  • easily sintered to conform with EN ISO 22674 2006 Class 4 metallic material for single and multiple units, and implant retained superstructures

  • CTE of 14.1 allows compatibility with a wide range of ceramics

COMPOSITION BEFORE AND AFTER SINTERING

(APPROXIMATELY 1% ORGANIC BINDER REMOVED COMPLETELY DURING SINTERING)

Co 63.0  Cr 29.0  Mo 6.0  Si, Fe, Mn, C <1 

 FREE FROM Be, Cd, Pb AND Ni

Above: CONCEPT 360® 'identical' frameworks before and after sintering. Ivoclar ceramic layering.

inert atmosphere argon sintering furnace

  • Argon atmosphere for sintering cobalt chrome

  • Open system and fully programmable

  • Adaptable for zirconia

As seen at IDS, Cologne, 2015